EP Conveyor Belt

Construction:

polyester conveyor belt is stuck together in sequence by many pieces of polyester sailcloth, which is covered by rubber and plastic owning good quality rubber cover up and down and good elasticity. Conveying small and not large massiveness materials, meanliness materials and biscuit materials. Applicable for conveying long and not very long distance materials, weight materials and materials that is vey long and its sliding rate is very fast.

Features:

With the advantages of thin belt with light weight, high tensile strength, fatigue and wear resistance, erosion resistance of water/steam/chemical, good impact resistance, excellent groove formation ability, low elongation, good stability ever heated and long service life, it’s the developing trend of fabric conveyor belt. It is mainly used in harsh condition of long distance, heavy-load, high-chemical corrosive etc, it is especially suitable for transporting in moist environment..

Fabric type	Fabric structure		Fabric type	Strength series					Cover thickness		Width	Length
	warp	weft		2ply	3ply	4ply	5ply	6ply	Upper	Lower
Polyester(EP)	Polyester(E)	Polyamide(P)	EP-80	160	240	320	400	480	2-12	1-5	350-2200	≤300
			EP-100	200	300	400	500	600
			EP-150	300	450	600	750	900
			EP-200	400	600	800	1000	1200
			EP-250	500	750	1000	1250	1500
			EP-300	600	900	1200	1500	1800
			EP-350		1050	1400	1750	2100
			EP-400			1600	2000	2400
			EP-500			2000	2500	3000

Standards	Cover rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply	Cover to Ply	Ply to Ply
DIN 22102	Mpa	%	mm3	N/mm (≤1.5mm)	N/mm (>1.5mm)	N/mm
DIN 22102-Z	15	350	250	3.5	4.5	5
DIN 22102-W	18	400	90	3.5	4.5	5
DIN 22102-Y	20	400	150	3.5	4.5	5
DIN 22102-X	25	450	120	3.5	4.5	5

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply	Cover to Ply	Ply to Ply
AS 1332	Mpa	%	mm3	N/mm (≤1.9mm)	N/mm (>1.9mm)	N/mm
AS 1332-N17	17	400	200	4	4.8	6
AS 1332-M24	24	450	125	4	4.8	6

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply	Cover to Ply	Ply to Ply
RMA	Mpa	%	mm3	N/mm (≤1.6mm)	N/mm (>1.6mm)	N/mm
RMA-I	17	400		3	4.4	4
RMA-II	14	400		3	4.4	4

Standards	Cover Rubber			Adhesion
	Tensile Strengtd	Elongation at break	Abrasion	Cover to Ply	Cover to Ply	Ply to Ply
SANS 1173	Mpa	%	mm3	N/mm		N/mm
A	18	400	70	5		7
C	20	400	150	5		7
M	25	450	120	5		7
N	17	400	150	5		7